MODIC™ Peelable for PET, HIPS, PVC, PP substrates
Grade | Z050F | Z051F | Z040F | Z041F | Z100F | Z200F | Z400F | ||
---|---|---|---|---|---|---|---|---|---|
Application | Blow Film | Blow Film | Cast Film Coating | Cast Film Coating | Cast Film Coating | Cast Film Coating | Special | ||
MFR | ISO R-1133 | g/10min | 2.4 | 2.4 | 7 | 21 | 12 | 17.5 | 4 |
Density | ISO R-1183 | g/cm3 | 0.90 | 0.93 | 0.91 | 0.91 | 0.91 | 0.92 | 1.1 |
Melting Point (Peak) | MCC method (DSC) | °C | 104 | 100 | 104 | 98 | 100 | 106 | 120 |
Tensile Strength At Yield | ISO-R-527 | MPA | - | 7 | 10 | 14 | 19 | 12 | 19 |
Tensile Elongation At Break | ISO R-527 | % | >500 | >500 | >500 | >500 | >500 | >500 | >500 |
Haze | ISO 14782 (30µmt) | % | 12 | - | 5 | - | 3 | 4 | - |
MODIC™ PEELABLE FOR PP substrate in higher temperature applications
Grade | X151F | X241F | X340F | X341F | X252F | V6043W | ||
---|---|---|---|---|---|---|---|---|
Application | Blow Film | Blow Film | Cast Film | Cast Film | Cast Film | Coating | ||
MFR | ISO R-1133 | g/10min | 2.1 | 2.7 | 12 (230°C) | 17 (230°C) | 5.3 | 9 |
Density | ISO R-1183 | g/cm3 | 0.91 | 0.90 | 0.90 | 0.90 | 0.90 | 0.90 |
Melting Point (Peak) | MCC method (DSC) | °C | 109 | 140 | 140 | 140 | 142 | 140 |
Tensile Strength At Yield | ISO-R-527 | MPA | 13 | 14 | 15 | NB | 11 | - |
Tensile Elongation At Break | ISO R-527 | % | >500 | NB | >500 | NB | 15 | - |
Haze | ISO 14782 (30µmt) | % | 9 | - | 16 | 16 | 50 | - |
Peel Strength | Low | High | High | High | Low | High | ||
Heat Resistance | °C | <100 | 121< | 121< | 121< | 121< | 121< |
Remarks:
Values only describe typical properties and may not be considered as specifications.
Not all grades are available in all regions, please contact your local sales representative.